GaAs, Growing Method: VGF (111)B, Si-doped, 2" dia x 0.35mm, 2sp - GASicB50D035C2US Cathode Polishing: two sides polished

Polishing:                          two sides polished

Please click on the pictures to learn more about each instrument or component individually

MTI will replace the unsatisfied substrate which has no film grown and no damage free of charge until you are satisfied within 15 days after receiving it

about 5 mm x 5 mm x 0

Two-wave mixing coupling constant: 10 -40  cm-1 Absorption loss:

GaAs, Growing Method: VGF (111)B, Si-doped, 2" dia x 0.35mm, 2sp - GASicB50D035C2US Cathode Polishing: two sides polishedGaAs single crystal wafer Growing Method: VGF Orientation: (111)B Primary Flat: EJ(0 11)+ 0. 5 deg; Secondary Flat: EJ( 211) Size: 2" dia x 0. 35mm Polishing: Two sides polished Doping: Si doped Conductor type: S C N Resistivity:(1. 5 4. 1)E 3 ohm. cm Carrier Concentration: (0. 6 2. 4)x10^18 c. c Mobility: 1750 2450 cm^2 V. S EPD: N A Ra(Average Roughness) : < 0. 4 nm Note: EPI ready wafers